Portable Hardness Tester

UCI probe types : 1kgf (10N) 2.2 lbf, 5kgf (50N) 11lbf, 10kgf (98N) Leeb probe types : D, DC, DL, C, D+15, E, G Measuring Range : HV:230~940; HRC:20~70; HB:90~650. Tensile strength, MPa 370~1740 Measuring Accuracy : HV:3%HV; HRC:1.5%HRC; HB:3%HB Indenter : Diamond Indenter (UCI), Hardened ball (Leeb) Measuring Direction : Any direction 360 Data Storage : Limited only by the memory card Communication : Upload data to PC and export as a spreadsheet (USB cable and software included ) Hardness Scale : HRC, HB, HV, HRB, HS, HL, MPa

HL display range: 0999HLD Accuracy: 6 HL(at 800HLD) Repeatability: 6 HL Testing direction: Any direction Measurement Range: 0-100 HA Display: Large LCD with back light Scales: HRB, HRC, HB, HV. HSD, MPa Power: dry cell (3 x1.5V AAA) Operating temperature: 00C +500C (320F 1220F) Storage temperature: 100C +600C (140F 1400F) Humidity: 5% 95% Dimensions: 150mm*80mm*24mm (5.9 x 3.1 x 0.9 inches) Weight: Approx.200g (display unit) Min. weight of test object: 5kg ( less than 5kg to 0.1kg must be coupled on solid support) Min. thickness of test object: 5mm (less than 5mm up to 3mm must be coupled) Min. thickness of layers: 0.8mm Measuring Range: HRC :19.8~68.5, HB :30 ~ 655, HV :80 ~ 976, HRB :13.5 ~ 99.6, HSD :26.4 ~ 99.5, Mpa :375 ~2639

Technical Specifications: -Measuring range:(170-960) HLD, (17-68.5) HRC, (19-651) HB, (80-976) HV, (30-100) HS, (59-85) HRA, (13-100) HRB -Measuring direction:360 -Hardness Scale: HL, HB, HRB, HRC, HRA, HV, HS -Display: segment LCD -Data memory: ax. 100 groups (relative to impact times 32~1) -Working voltage:3V (2 AA size alkaline battery) -Continuous working period: about 100 hours (With backlight off) -Communication interface:RS232 Main Application -Die cavity of molds -Bearings and other parts -Failure analysis of pressure vessel, steam generator and other equipment -Heavy work piece -The installed machinery and permanently assembled parts. -Testing surface of a small hollow space -Material identification in the warehouse of metallic materials -Rapid testing in large range and multi-measuring areas for large-scale work piece

Technical Specifications: -Measuring range:(170-960)HLD,(17-68.5)HRC,(19-651)HB,(80-976)HV,(30-100)HS,(59-85)HRA,(13-100)HRB -Measuring direction:360 -Hardness Scale:HL,HB,HRB,HRC,HRA,HV,HS -Accuracy: 6HLD -Display: segment LCD -Data memory: max. 100 groups (relative to impact times 32~1) -Working voltage: 3V (2 AA size alkaline battery) -Continuous working period: about 100 hours (With backlight off) -Communication interface: USB

Measuring range : HLD (170-960),HRC (17.9-69.5),HB (19-683),HV (80-1042),HS (30.6-102.6),HRA(59.1-88),HRB (13.5-101.7) Impact Directions : Up, down, horizontal, slanting up, slanting down Measuring Materials : Steel and cast steel, alloy tool steel, stainless steel, gray cast iron, nodular cast iron, cast aluminum alloy, copper zinc alloys (brass), an alloy of copper and tin, copper (bronze), forged steel Standards : ASTM A956,DIN50156-1,GB/T17394-1998 Hardness Scales : HL, HB, HRB, HRC, HRA, HV, HS. Tensile Strength : 374 to 2652 N/m 2 Display : 128*64 digital matrix LCD Memory : 600 groups max.(relative to impact times 32~1) Work Voltage : 9V/500mA.

MHT200 is a small, light and portable tester. It is most suitable for testing of heavy, big or outdoor metal parts. It can measure in any direction and also easy to be used and accurate on curved test surfaces. Especially, it can automatically compensate effect of weight which according to the test direction.